简介：SiliconoxynitridewasaddedinshapedAl2O3-SiC-Crefractorymaterialtoimprovetheslagresistanceinthispaper.Optimumaddingquantityofsiliconoxynitridepowderwasalsostudied.TheresultsshowthattheslagresistanceofAl2O3-SiC-Cshapedrefractoryisimprovedwhen2%or3%Si2N2Oisadded.AreasonableamountofSi2N2OaddedintoAl2O3-SiC-Cshapedrefractorycanproducesiliconoxideintotheslag,whichcanimprovetheviscosityofslagandpreventtheslagerosionandpenetration.

简介：

简介：

简介：

简介：AnO'-Sialon-Al2O3compositerefractorywaspreparedbyinsitureactionofSi3N4-ZrSiO4-Al2O3mixturewithfusedaluminaaggregates.Densification,insitureactionprocedureandmicrostructureofthematerialwereinvestigatedbymeansofX-raydiffraction,opticalandscanningelectronicmicroscopesandEDAX.

简介：Siliconcarbide(SiC)-alumina(Al_2O_3)-mullite(Al_6Si_2O_(13))compositepowderwassuccessfullysynthesizedat1550℃for5hviacarbothermalreductionreaction,andtheeffectsofvariousmassratiosofactivecarbontoflyash(0.38,0.44and0.58)onthephasecompositionandmicrostructureofproductswereinvestigated,andtheformationprocessofthepowderwasalsoanalyzedindetail.Theproductsmainlyconsistofβ-SiC,α-Al_2O_3,Al_6Si_2O_(13)andFeSi.IncreasingcarboncontentfavorsthedecompositionofAl_6Si_2O_(13)andformationofSiC.Theaverageparticlesizeofβ-SiCandα-Al_2O_3isabout1μmandthatofAl_6Si_2O_(13)is5-10μm.TheformationprocessofSiC-Al_2O_3-Al_6Si_2O_(13)powderincludesthedecompositionofmulliteinflyashandformationofSiC.

简介：EffectsofAl—Siadditiononhotmodulusofrupture（HMOR）,thermalshockresistanceC3andAlN:SireactswithCtoformSiC.Ultimately,in-situformednonoxidesincreaseappreciablywithtemperaturerisingandarewellinterlacedinpericlaseskeletonstructureat1300-1400℃.whichisbeneficialtothermomechanicalproperties.

简介：

简介：

简介：Simplethree-pointbendingtestatambienttemperaturecharacterizedthemechanicalbehaviorofburnedAl2O3-Crefractoriesbeforeandafterthermalshockinassociationwiththeprocessingparameters(graphitecontentandcokingtemperature,etc.).Theresultsshowedthatnon-linearplastic-elasticbehaviorunderloadlowerthancoldmodulusofrupture(CMOR)wasregisteredinallspecimensandreallinearelasticbehaviorcouldbeidentifiedafterthefirstload.Thetotaldeformationcouldbedividedintotwoparts,plasticandelasticareas.ThegraphitecontentandjointbondingsystemofcarbonandceramicphaseswereresponsibleformechanicalbehaviorofAl2O3-Crefractories.

简介：

简介：Inthisstudy,inordertoevaluatetheperformanceofhomogenizedbauxite,twoAl_2O_3-SiC-Ccastableswerepreparedusinghomogenizedbauxiteandbrownfusedcorundumasaggregates,respectively.5mass%andalusitewasintroducedintothetwocastablessoastoresearchtheeffectandmechanismofandalusiteinAl_2O_3-SiC-Ccastables.Theresultsshowedthat:(1)comparedwiththebrownfusedcorundumbasedcastables,thehomogenizedbauxitebasedcastableshadhighercoldstrengthafterheattreatment,butlowerhotmodulusofrupture;(2)additionof5mass%andalusitecouldenhancethecoldandhotmodulusofrupture,improvethethermalshockresistance,andoptimizethemicrostructureofspecimens;(3)themullitizationofandalusitewasnotobviousinthecastablesfiredat1100-1400℃.

简介：ThispapertestifiesthataluminiumandsiliconaswellastheircarbidexandnitridescanreactwithCOincarbon-containingzonetoformAl2O3andSiOgasthroughexperimentandthermodyanmicanalysis,ThegasesdiffusetooxidizedzoneandreactwithoxidizerssuchasCO2,Asaresult,Al2O3andSiO2aredepositedfromthegases,wihichblockthepores,thusreducetheamountofgasdiffusionandincreaseoxidationresistnaceofcarbon-containingmaterials.

简介：

简介：ThemagnesiabasedcurablespecimenswithdifferentSi3N4contentswerecastedusingsinteredmagnesite(w(MgO)=95%)asstartingmaterial,SiO2micro-powderasbinder,0.3%,4%and5%β-Si3N4powderreplacingtheequaladditionofmagnesiapowderrespectively.Theslagresistancetestwascarriedoutat1550℃for3husingBaosteeltundishslagandstaticcruciblemethod.Theresultindicatesthat:introducingSi3N4couldobviouslyimprovetheslagresistanceofMgObasedcastable,whichincreasedwithincreasingSi3N4.DenseSiO2sinteredlayerformedonthesurfaceofmagnesiabasedcastablebecauseoftheoxidationofSi3N4addition,whichcanpreventthefurtherslagpenetration.Inthedeepinnerofcastable,thepartial-pressureofoxygenwasverylow,soSi3N4canexiststably.Meanwhileinreducingatmosphere,Si3N4washardtobesintered,whichresultedinthelooseinteriorstructureofMgObasedcastable.

简介：Si3N4powderandhot-pressedSi3N4ceramicsaddedwithAl2O3areusedforinvestigatetheiroxidationbehviorinairandnitrogenatmosphere(withoxygenpartialpressurePO2=1-10Pa),TheoxidationproductsofSi3N4areexaminedbychemicalanalysi,X-raydiffraction(XRD)andXPSmethod,Also,thermodynamiccalculationismadetoanalyzeoxidationbehaviorofSi3N4.TheresultsshowthatonlypassiveoxidationwilloccurwhenSi3N4isoxidizedinairathightemperature,whereasinN2athightemperature,theactiveoxidationisdominantinspiteoftheexistenceofalittlepassiveoxidation.

简介：ThemechanicalpropertiesofpressurelesssinteringFe-Si3N4bondedSiCandSi3N4bondedSiCwithsamemanufactureprocesshavebeencomparedinthispaper.TheoxidizingmechanismofFe-Si3N4bondedSiCceramicmatrixcompositehasbeeninvestigatedespeciallythroughTG-DSC(thermogravimetricanalysis-differentialscanningcalorimeter)experiment.DuringoxidationprocedurethemainreactionistheoxidationofSiCandSi3N4,SiO2whichformprotectingfilmtopreventfurtheroxidizing.AndresidualironinthesamplesbecomeFe2O3andFe3O4,theoxidationkineticsat1100～1300℃ofre-Si3N4bondedSiChasbeenstudiedespecially.Theweightgainperunitareaatinitialstagechangesaccordingtobeelinerule,inthemiddleaccordingtoconic,andinthelastoxidationperiodfollowsparabolarule.

简介：MgO-Al2O3-Cr2O3rammingmixesmadeofdifferentrawmaterialshavedifferentmineralstructureanddifferentphysicalpropertiesthoughwiththeidenticalparticlesizedistribution,thesameamountofbinderandchemicalcomposition.Theresidualcarboncontentofthefusedmagnesia-chromematerialmadeinreducingatmosphereisveryhigh,ifthismaterialsisusedintheMgO-Al2O3-Cr2O3rammingmix,itwouldcausespallingofthefurnaceliningduringdrying-out.

简介：DenseSi3N4BNcompositeceramicswerefabricatedbysparkplasmasinteringat1500,1600and1650℃under50MPafor5minusingSi3N4andBNpowdersasstartingmaterialsand2mass%Al2O3and6mass%Y2O3assinteringadditives.ThevolumefractionofBNinSi3N4BNcompositepowderswaschosenas10%,20%,and30%,respectively.TheresultsofXRDandSEMshowthatα-Si3N4completelyturnsintoβ-Si3N4whenthecompositeceramicsaresinteredat1650℃;theadditionofBNhindersthegrowthofSi3N4grains,refiningthestructure;VickershardnessandfracturetoughnessofthecompositeceramicsdecreasewiththeincreaseofBNcontent.

简介：Inthispaper,theinflucnceofchiefprocessparametersontheontinuousproductionofSi3N4powderbyrenitridationhasbeenstudied,Thesutiableprocessparametershavebeenfound,andhighqualitySi3N4powderhasbeendeveloped.