简介：Mechanicalalloying(MA)andsubsequentsolidsinteringprocesswasusedtopreparetheNd-containingmagnetostrictiveTb0.4Nd0.6(Fe0.8Co0.2)1.90alloy.Thestructure,thermalstabilityandphasetransformationwereinvestigatedasfunctionsofcomposition,millingprocessandannealingtemperature.Anamorphousphasewasformedbyhigh-energyballmillingfor5hwiththeball-to-powderweightratioof20:1,whichcrystallizedintoMgCu2-typeandPuNi3-typecrystallinestructurewithdifferentannealingte...

简介：Flexiblethin-filmsupercapacitorswithhighspecificcapacitancearehighlydesirableformodernwearableormicro-sizedelectricalandelectronicapplications.Inthiscontribution,Ni-Cohydroxides(NCH)nanosheetsweredepositedontopofNi-Cualloy(NCA)nanowirearraysformingafreestandingthin-filmcompositeelectrodewithhierarchicalstructureforsupercapacitors.Duringelectrochemicalcycling,thedissolutionofCuintoCuionswillcreatemoreactivesitesonNCA,andtheredepositedcopperoxidecanbecoatedontoNCH,givingrisetosubstantialincreaseinspecificcapacitancewithcycling.Meanwhile,NCAandNCHhaveexcellentconductivity,thusleadingtoexcellentrateperformance.Thisflexiblethin-filmelectrodedeliversanultrahighinitialspecificcapacitanceof0.63F·cm~(-2)(or781.3F·cm~(-3)).Duringcharge-dischargecycles,thespecificcapacitancecanincreaseupto1.18F·cm~(-2)(or1475F·cm~(-3))alongwiththe'self-etching'process.Theelectrodepresentsabetterspecificcapacitanceandratecapabilitycomparedwithpreviouslyreportedflexiblethin-filmelectrode,andthisnoveldesignofetchingtechniquemayexpandtootherbinaryorternarymaterials.

简介：本研究通过使用光电直读光谱仪,采用类型标准化法对2024铝合金的化学成分进行研究,建立工作曲线,并确定最优化的分析线和工作条件,考察该方法的精密度和准确度。试验结果表明：在优化的试验条件下,8种元素测定值的相对标准偏差（n=10）均小于5.58%。该方法用于2024铝合金实际样品分析,测定结果与ICP分析测定结果相一致。利用光电直读光谱仪建立类型标准化工作曲线分析检测快速准确、仪器稳定,可用于日常分析。

简介：针对23Co14Ni12Cr3Mo超高强度钢材料,研究喷丸强化对其表面性能的影响。采用扫描电镜、白光干涉仪等设备,分析喷丸强化对试样表面形貌、粗糙度、硬度、残余应力、元素含量等的影响。结果表明:喷丸强化后,试样表面留有大量弹坑,产生明显塑性变形;表面粗糙度增大,算术平均粗糙度为1.33μm;硬度显著增大,最表层硬度由喷丸前的HV476增加至HV497,硬化层深度约150μm;试样表层的残余压应力值由375MPa增加至475MPa,最大残余压应力值约518MPa,位于距表面50μm深度处,喷丸形成的残余压应力层深度约为134μm;喷丸后试样中C、Si、Cr等各元素的质量分数均略有增加。喷丸在一定程度上改善了23Co14Ni12Cr3Mo钢材料的表面性能,有利于提高其疲劳抗力和耐腐蚀性。

简介：通过气雾化方法制备Al86Ni7Y4．5Co1La1.5（摩尔分数，％）合金粉末。首先，将粉末进行不同时间的球磨，然后在不同的烧结温度及保压时间等条件下对粉末分别进行热压烧结和放电等离子烧结。通过X射线衍射仪（XRD），扫描电镜（sEM）以及透射电镜（TEM）对粉末和块体材料的显微组织和形貌进行表征。结果表明：在特定球磨参数下球磨100h以上可以产生非晶，而且通过放电等离子烧结可以得到非晶／纳米晶块体材料，然而这种材料的相对密度较低。通过热压烧结可制备抗压强度为650MPa的Al86Ni7Y4．5Co1La1.5纳米块体材料。

简介：研究Zr添加对Al-Mn-Si-Zn合金显微组织、力学性能及电化学性能的影响。透射电镜观察表明,Zr合金化可使退火态合金中的析出相更加细小、弥散,但是对模拟钎焊态合金的影响较弱。拉伸实验结果表明,添加Zr能够显著提高退火态合金的力学性能,但是对模拟钎焊态合金影响不大。电化学实验结果则表明,Zr元素的添加可降低退火态合金的抗腐蚀性能,但是对模拟钎焊态合金的影响不大。

简介：ThestructureandelectrochemicalpropertiesofanewlowcobalthydrogenstorageelectrodealloysLa1-xLixNi3.2Co0.3Al0.3(0≤x≤0.2)wereinvestigatedwithadifferentadditionsofLiinreplacementofLa.WiththeincreaseofLicontentsthemaximumdischargecapacityincreasesfrom240mAh·g-1(x=0)to328.4mAh·g-1(x=0.1)andthecyclestabilityisimprovedcorrespondingly.ThecapacitydecaycanremaiN28.6%(x=0.2)after230charge/dischargecycles.Thehighratedischarge(HRD)abilityofthealloys(x≤0.1)isimprovedandthebestHRDis34.1%(x=0.1)underthedischargecurrentdensity1200mA·g-1.ItisfoundthatthepreparedalloysarebasicallycomposedofLaNi5asmatrixphaseandLaNi3assecondphase(x≤0.1).ButtheabundanceofLaNi3phasedramaticallydecreaseswithincreasingx.Whenx=0.2,anewphaseAl(NiCo)3isformed.

简介：研究了立方碳化物Cr3C2、VC以及稀土La添加剂对WC-Co合金中WC晶粒形貌以及合金硬度与韧性的影响。为了强化烧结过程中WC晶粒生长的驱动力,采用具有高烧结活性的纳米W和纳米C为原料。为了获得合金中WC晶粒的三维形貌,采用扫描电镜直接观察合金烧结体的自然表面。结果表明,合金添加剂对WC晶粒形貌及其粒度分布特征以及合金的硬度与韧性有较大影响。由于均质三角棱柱形板状WC晶粒的形成,WC-10Co-0.6Cr3C2-0.06La2O3合金具有极佳的硬度与韧性组合。讨论了合金中WC晶粒形貌的调控机制以及合金中WC晶粒形貌特征对合金性能的影响。

简介：EmployingLi2CO3,NiO,Co3O4,andMnCO3powdersasstartingmaterials,Li[Ni1/3Co1/3Mn1/3]O2wassynthesizedbysolid-statereactionmethod.Variousgrindingaidswereappliedduringmillinginordertooptimizethesynthesisprocess.Aftersuccessiveheattreatmentsat650and950℃,thepreparedpowderswerecharacterizedbyX-raydiffraction(XRD)analysis,scanningelectronmicroscopy,andtransmissionelectronmicroscopy.Thepowderspreparedbyaddingsalt(NaCl)asgrindingaidexhibitaclearR3mlayerstructure.ThepowdersbyothergrindingaidslikeheptaneshowsomeimpuritypeaksintheXRDpattern.Theformerpowdersshowauniformparticlesizedistributionoflessthan1μmaveragesizewhilethelattershowsawidedistributionrangingfrom1to10μm.EnergydispersiveX-ray(EDX)analysissshowthattheratioofNi,Co,andMncontentinthepowderisapproximately1/3,1/3,and1/3,respecively.TheEDXdataindicatenoincorporationofsodiumorchlorineintothepowders.Charge-dischargetestsgaveaninitialdischargecapacityof160mAh·g-1forthepowderswithNaCladditionwhile70mAh·g-1forthepowderswithheptane.

简介：以CaSO4制备得到的CaS为还原剂,研究氧化锰矿的还原-酸浸过程,考察硫化钙与矿石的质量比、还原温度、还原时间、液固比、搅拌速率、浸出温度、浸出时间和H2SO4浓度对氧化锰矿中锰及铁浸出率的影响。结果表明：优化的还原工艺条件为硫化钙与矿石质量比1：6.7、液固比5：1、搅拌速率300r/min、还原温度95°C、还原时间2.0h;酸浸工艺条件为搅拌速率200r/min、H2SO4浓度1.5mol/L、浸出温度80°C、浸出时间5min。在此优化条件下,锰的浸出率达到96.47%,而铁的浸出率仅为19.24%。该工艺可以应用于不同类型氧化锰矿中锰的提取,且锰的浸出率均高于95%。

简介：采用丝印法在铝基板上制备具有低室温电阻率、适中热敏常数的负温度系数BaCo0.02ⅡCo0.04ⅢBi0.94O3/Ba0.5Bi0.5Fe0.9Sn0.1O3复合热敏厚膜。采用数字多用表、吉时利2400和阻抗分析仪对热敏厚膜的电学性能进行表征。结果表明：随着Ba0.5Bi0.5Fe0.9Sn0.1O3含量从0.05增加至0.25,厚膜的室温电阻率、热敏常数和峰值电压均有所增加且分别处于1.47-26.5Ω·cm、678-1345K和18.9-47.0V范围内,厚膜峰值电压对应的电流也有所降低且处于40-240mA范围。阻抗谱测试表明,这些热敏厚膜表现出非正常的异质电学微结构行为,由高阻态的晶粒和较低电阻态的晶界区域构成。由此可知,在BaCo0.02ⅡCo0.04ⅢBi0.94O3中添加Ba0.5Bi0.5Fe0.9Sn0.1O3改善了热敏行为但也恶化了电流特征.

简介：采用固相烧结方法制备Mg2Ni0.7M0.3(M=Al,Mn,Ti)合金。利用X射线衍射仪、扫描电镜和扫描透射电镜对合金的相组成和显微组织进行系统表征。结果发现,Mg2Ni0.7M0.3合金中形成了具有面心立方结构的金属间化合物Mg3MNi2,其与Mg和Mg2Ni共存;且M原子半径与Mg原子半径越接近,越有利于Mg3MNi2的形成。采用Sievert和Tafel方法对Mg2Ni0.7M0.3合金的储氢性能和耐腐蚀性能进行研究。Mg2Ni0.7M0.3合金的吸/放氢性能得到明显改善。Mg2Ni0.7Al0.3、Mg2Ni0.7Mn0.3和Mg2Ni0.7Ti0.3合金的脱氢反应的激活能较Mg2Ni的激活能明显降低,分别为-46.12、-59.16和-73.15kJ/mol。与Mg2Ni合金相比,Mg2Ni0.7M0.3合金的腐蚀电位向正方向移动,如Mg2Ni0.7Al0.3合金(-0.529V)与Mg2Ni合金(-0.639V)的腐蚀电位差为0.110V,表明添加Al、Mn和Ti能使合金的耐腐蚀性能得到显著提高。