简介：Hexagonplate-likeAl8B4C7powdersweresuccessfullysynthesizedusingamixtureofdiborontrioxide,activatedcarbonandaluminumoraluminabyacarbothermalreductionprocess.TheeffectofAlsourceandstartingmaterialsadditionsonsynthesisofAl8B4C7wasinvestigated.ThephasecompositionandmicrostructureofAl8B4C7powderwerecharacterizedbymeansofXRD,SEMandEDS.ThemainphasecompositionsoftheproductssynthesizedfromAl,B2O3andactivatedcarbonareAl8B4C7andAl2OC.Al2O3canreplaceAltosynthesizeAl8B4C7.Al8B4C7grainssynthesizedfromAl2O3,B2O3andactivatedcarbonarehexagonplate-likeandhaveathicknessof10μmandasizeofabout100μm.

简介：

简介：

简介：Theroleofnano-SiO2andultra-fineboroncarbideonthepropertiesofalumina-graphitematerialswasinvestigated.Thestudyshowedthattheultra-fineboroncarbideaddedmodifiedthemicrostructureofresidualcarbonandpromotedthechemicalbondbetweenresidualcarbonfromphenolicresinandflakegraphite.Thecarbonwhitecouldstrengthentheresidualcarbonfromphenolicresin.ThesetwoadditivesimprovedthemechanicalpropertiesofAGrefractoriesatbothroomtemperatureandhightemperature,andthermalshockresistancewasimprovednoticeably.Whenthetwoadditivesweredopedtogether,carbonwhitecouldretardtheevaporationofB2O3.Thermalshockresistancewasguaranteedwithasmalleramountofultrafineboroncarbide.

简介：

简介：Siliconcarbide(SiC)-alumina(Al_2O_3)-mullite(Al_6Si_2O_(13))compositepowderwassuccessfullysynthesizedat1550℃for5hviacarbothermalreductionreaction,andtheeffectsofvariousmassratiosofactivecarbontoflyash(0.38,0.44and0.58)onthephasecompositionandmicrostructureofproductswereinvestigated,andtheformationprocessofthepowderwasalsoanalyzedindetail.Theproductsmainlyconsistofβ-SiC,α-Al_2O_3,Al_6Si_2O_(13)andFeSi.IncreasingcarboncontentfavorsthedecompositionofAl_6Si_2O_(13)andformationofSiC.Theaverageparticlesizeofβ-SiCandα-Al_2O_3isabout1μmandthatofAl_6Si_2O_(13)is5-10μm.TheformationprocessofSiC-Al_2O_3-Al_6Si_2O_(13)powderincludesthedecompositionofmulliteinflyashandformationofSiC.