简介:Moleculardynamicssimulationswereperformedtostudytheinteractionbetweenatomichydrogenandsiliconcarbide.Inthepresentstudy,wefocusontheeffectofthesurfacetemperatureonHinteractingwithsiliconcarbide.ThesimulationresultsshowthattheretentionofHatomsinthesampledecreaseslinearlywithincreasingsurfacetemperature.ThedepthprofileanalysisshowsthatthesampleismodifiedbyHbombardment,andthedensityofHatomsisgreaterthanthoseofSiandCatomsneartheinterfaceregionbetweentheH-containingregionandthebulk.However,nearthesurfaceregionthedensitiesofH,SiandCatomsarealmostequivalent.Inthemodifiedlayer,thebondsconsistofSi-CandSi-HandC-H.ThefractionofSi-Cbondsisthegreatest.OnlyafewC-Hbondsarepresent.