简介:Ni2P/ZrO2-SBA-15catalystswithdifferentzirconiumn-propoxide/SBA-15massratiosweresynthesizedtoevaluatetheirdibenzothiophenehydrodesulfurizationcatalyticactivity.EffectofZrO2introductionwasinvestigated.SupportsandcatalystswerecharacterizedbyBET,XRD,29SiNMR,XPSandFTIR.TheresultsindicatedthatzirconiumwasincorporatedintoSBA-15intheformsof[(–O–)2Si(–O–Zr)2]and/or[(–O–)3Si–O–Zr],andthattheSBA-15frameworkstructurewasmaintainedafterincorporationofZrO2.Withzirconiumcontentincreasing,ZrO2wastransformedfromamorphousphasetotetragonalphase.ZirconiumincorporationintoSBA-15supportscouldfacilitatetoformmoredispersedNi2Pactivephase.TheremightbesomeinteractionoccurringbetweenthePandZrspecies.InadditiontoNi2P,anotherkindofactivephase,ZrP,wasformed,whichmightexhibitabetterHDSactivitythanNi2P.Itwasobservedthatatatemperatureof280°C,pressureof3.0MPa,WHSVof6.5h?1andH2tooilratioof450,theNi2P/Zr-SBA(1.5)catalyst,where1.5representszirconiumn-propoxide/SBA-15massratio,showedthehighestDBTconversion,whichwas86.6%,almost35%higherthanthatoftheNi2P/Zr-SBA(0)catalyst.
简介:以占空比、脉冲频率、电流密度、镀液温度为优化工艺参数,以镀层表面硬度、结合强度、磨损量、腐蚀速率为综合优化工艺目标,运用改进的TOPSIS法对脉冲电沉积Ni-P-W合金工艺参数进行优化。优化结果为:占空比30%、脉冲频率250Hz、电流密8A/dm2、镀液温度60℃。采用优化工艺参数进行脉冲电沉积Ni-P-W合金与最优试验设计组相比,表面硬度提高了8.14%,结合强度提高了5.32%,磨损量减小了4.26%,腐蚀速率减小了6.25%。
简介:文章通过空间正义理论对邻避冲突问题进行分析发现,邻避设施供给必须实现公共价值追求的目标正义、负外部效应均衡分担的工具正义以及公众参与和风险沟通的过程正义等三大要件的有机统一。对武汉市某临终关怀医院项目建设的案例分析表明,当存在着过度追求经济效应、负外部性非均衡转嫁、公众低度参与以及风险沟通不足等空间生产非正义情形时,邻避设施供给就会引发邻避冲突,甚至演变为以"封路维权""街头散步"等为标志的空间抗争事件。案例研究还发现,实现邻避设施供给的正义性要件,应当由政府和公众共同讨论来决定公共价值的边界范围,构建起公民全参与和风险持续沟通的决策机制,以"空间正义"为议题搭建起协商式补偿机制,消除不同主体对空间生产价值追求不一致造成的冲突。
简介:作为科研界的储备力量,研究生群体的学术不端行为受到广泛关注,但救济渠道较为缺失。对研究生学术不端处罚进行救济具有一定的法律依据,包括《中华人民共和国宪法》、行政法、教育部规章、高校自制学术规范,但对救济的具体措施总体缺位。当前在实践中,采取行政诉讼、行政复议的维权救济方式成功率低、采用量小,使学生更愿意通过法律以外的途径进行救济,包括校内求助与校外求助。通过法律与实践的经验分析,"C9联盟"各高校在研究生救济方面普遍存在程序正义的保障力度参差不齐、制度调整对象的差异性区分不足、与我国科技法律的谦抑性要求尚有差距等问题,需要由此进行针对性改革。