简介:Heterogeneousprecipitationmethodwasusedtopreparedsurfacecoatingonself-madeBaMgAl10O17:Euphosphor.Resultsillustratethatthecoatingfilmcanbesilicondioxideinamorphousstatewith50nminthickness.Photoluminescenceresultsindicatethatthecoatinglayerpresentsanobservableimprovedeffectontheenhancementofthermalstability.Whenbakedat600℃for1h,theluminanceofcoatedBAMkeepsat92%higherthanthatofuncoatedBAMby23%.ThisprotectiveeffectcanbeattributedtothehighcompactdegreeanduniformityofthisamorphousSiO2coatingfilmwhichisservedasadiffusionblocklayertoinbreakoxygenatom,thusreleasestheoxidationextentofEu2+effectively.
简介:SinglephaseofBa1-xMgAl10O17:xEu2+(0.02≤x≤0.14)phosphorswasfirstsuccessfullypreparedbyco-precipitationinaqueousmediumwitha'reversestrike'method,usingoxalicacidandammoniatogetherasprecipitants.Completelycrystallizedphosphorswereobtainedat1300℃,whichis300℃lowerthanthetemperatureofsolid-statereaction.TheirphotoluminescencewasinvestigatedunderUVandVUVregion,respectively.TheemissionspectraofBa1-xMgAl10O17:xEu2+samplesexcitedby254or147nmshowedacharacteristicwidebandwiththepeakcentredatabout450~454nm.Optimumemissionintensityreachedatx=0.1andthenconcentrationquenchingoccurred.Thesynthesizedphosphorshows10%higheremissionintensitythanthatpreparedbysolid-statereaction.
简介:TheNd60Fe20Al8Co10B2alloywaspreparedbysuctioncastingofthemoltenalloyintoacoppermoldunderargonatmosphere.Themicro-structuralandmagneticpropertychangesintheNd60Fe20Al8Co10B2alloyduringcrystallizationwereinvestigatedbyX-raydiffraction(XRD),differentialscanningcalorimetry(DSC),scanningelectronmicroscope(SEM)andthevibratingsamplemagnetometer(VSM).TheprecipitationandNd-richandFe-richphaseshavenosignificanteffectontheintrinsiccoercitityforNd60Fe20Al8Co10B2alloyannealedbelow723K.However,thegrowthofFe-richphasedecreasesthesaturatemagnetizationandremanenceofthealloy.Thehardmagneticbehaviorisdisappearedwhenthealloyisfullycrystallized.