简介:Thestressintensityfactor(SIF)isacriticalparameterassociatedwiththefracturebehaviourofmaterials.Inthispaper,weselectthedisplacementfunctionaroundacracktipastheshapefunctionofthedigitalimagecorrelation(DIC),whichmakesitpossibletodirectlycalculatetheSIFbythecorrelationscheme.Moreover,weuseanon-rectangularsubset,whichcanreducetheinfluenceofplasticdeformationandcrackwidthontheDICmeasurementaccuracy.WemeasuredtheSIFofamodeIcrackinasuper-hardaluminiumalloyspecimentoverifytheperformanceoftheproposedmethod.OurexperimentalresultsshowthataDICwithaspecificshapefunctioncanbeusedtoaccuratelyandefficientlycalculatetheSIF.Furthermore,wealsopresentapracticalapplicationofourproposedmethodfordeterminingtheSIF,crackpropagationangleandcracktipdisplacement.