简介：

简介：Theeffectofnonmetallicinclusionsinthedropletofthestainlesssteelcoveredelectrodeontheporositywasresearched.Theresultshowsthatthenonmetallicinclusionsinthedropletarespherical,theircompositionisdifferentfromtheoneofslagandtheinclusionshavethecharacterof"innerformation".Whentheratioofrutiletoilmeniteinthecoatedmaterialisincreased,thedropletbecomescoarse,thecontentofnonmetallicinclusioninthedropletdecreases,andtheporositysensitivityintheweldmetalalsodecreases.Whentheratiooffledspartoilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusioninthedropletincreases,andtheporositysensitivityintheweldmetalincreases.WhentheratioofFe2O3toilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusiondecreases,whiletheporositysensitivitydoesnotreduce.

简介：WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability，evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.

简介：ThesusceptibilityofweldedjointfortheX65pipelinesteeltoH2Sstresscorrosioncracking(SCC)isinvestigated.SCCtestsonthesteelarecarriedoutintheenvironmentbasedonNACETM-01-77solutionwithsaturatedgaseousH2S.Thethresholdstressintensityfactorandcrackpropagationvelocityarecalculatedaccordingtowedge-openingloading(WOL)specimens.Thethree-dimensionalelastic-plasticfiniteelementanalysisofWOLspecimensisperformedbyusingtheFEMprogrammingpackageANSYS.Stressfieldandconcentrationofhydrogendistributionpropertyaheadofthecracktipareobtained.ThispapersurveyedthemicrostructureofweldedjointandstudiedonthemechanicalpropertiesofX65pipelinesteel.Itprovidesexperimentalbasisforstudyingstresscorrosion.Theresultsofnumericalanalysisareconsistentwithconclusionsofstresscorrosiontest.