简介:PrecipitationstudywascarriedoutinNi-35at.pctCralloybymeasuringelectricalresistivityatdifferentageingtemperaturesandlongageingtimes.Duringageing,itwasobservedthatelectricalresistivityinitiallyrosewithageingtimeandthenfellafterverylongageingataconstanttemperature.TheinitialincreaseinresistivityduringageingmaybeattributedtotheformationofGPzones/Cr-richprecipitatesatearlystagesbynucleationprocessanddecreaseinresistivity,andafterattainingamaximum,isduetothegrowthofprecipitateparticlesandsubsequentlybycoarseningoftheseprecipitates.TheresultsofelectricalresistivitymeasurementsduringageingwereconfirmedbyX-raydiffractionanalysisindicatingtheformationofaCr-richphaseandaCr3Ni2phaseintheNimatrix.
简介:结果证明Mg在空间在钢的张力的性质和坚硬上有更少的效果温度,而是Mg的正确数量改进影响和破裂坚韧并且减少破裂转变温度更加由于包括修正,象一样通过加强谷物边界并且修改边界碳化物戏剧性地延长槽口压力破裂生活。有一个最佳Mg内容,它在试验性的35CrNi3MoV钢是大约0.0030%。(编辑作者摘要)8个裁判员。
简介:WehavestudiedtheMossbauereffectofYBa2Cu2.88Fe0.12O7-xsuperconductiveoxidefrom78to273K.TwominimaofrecoillessfractionandDebyetemperaturewerefoundnear110Kand220K.Itmeansthatlatticesofteninghappenednearthesetwotemperatures.Wealsoobservedminimaofisomershiftnear110Kandquadrupolesplittingincreasewhentemperatureislowerthan110K.Wesuggestthatlatticesofteningwouldleadtothedisplacementofoxygenatoms.Thismayberelativetosuperconductivetransition.
简介:InvestigationhasbeencarriedouttofindtheeffectsofNdsubstitutionandCuadditiononthehydrogenstoragepropertiesofAB5-typealloywithamulticomponentLa0.6M0.4Ni4.8Mn0.2(M=Y,Nd)system.La0.6Y0.4Ni4.8Mn0.2,whichwasusedinanair-conditioningsystem,showedpoorhysteresisandslopingcharacteristics,whichledtoadecreaseconcerningthecoefficientofperformanceofthesystem.BythesubstitutionofNdforY,thehydrogenstoragecapacityincreased,andtheplateaupressuredecreasedalittle,butthehydrogenabsorptionkineticsdecreaseddramatically.CuadditioncaneffectivelyimprovethekineticsofhydrideformationwithoutchangingthehydrogenstoragecapacityofLa0.6Nd0.4Ni4.8Mn0.2.IthasbeenfoundthatLa0.6Nd0.4Ni4.8Mn0.2Cu0.1alloyshowedgoodhydrogenstoragecharacteristicsformetalhydrideair-conditioningsystem.Theresultsshowedthat,foreachcomponentofLa0.6Mo.4Ni4.8Mn0.2,theeffectivehydrogenstoragecapacityincreasedwithdecreaseoftheunitcellparameterc/aandthehydrogenabsorptionplateaupressureincreasedwithdecreaseoftheparametera.
简介:Thepresentstudyisconcernedwiththeeffectoffillermetalssuchasausteniticstainlesssteel,ferriticstainlesssteelandduplexstainlesssteelontensileandimpactpropertiesoftheferriticstainlesssteelconformingtoAISI409Mgrade.Rolledplatesof4mmthicknesswereusedasthebasematerialforpreparingsinglepassbuttweldedjoints.Tensileandimpactproperties,microhardness,microstructureandfracturesurfacemorphologyofthejointsfabricatedbyausteniticstainlesssteel,ferriticstainlesssteelandduplexstainlesssteelfillermetalswereevaluatedandtheresultswerereported.Fromthisinvestigation,itisfoundthatthejointsfabricatedbyduplexstainlesssteelfillermetalshowedhighertensilestrengthandhardnesscomparedtothejointsfabricatedbyausteniticandferriticstainlesssteelfillermetals.Jointsfabricatedbyausteniticstainlesssteelfillermetalexhibitedhigherductilityandimpacttoughnesscomparedwiththejointsfabricatedbyferriticstainlesssteelandduplexstainlesssteelfillermetals.