简介：以PbO，MgO，Nb2O5，TiO2为原料，采用两步固态反应法制备了纯钙钛矿相的0．92PMN-0．08PT陶瓷，并对其相的组成、微观形貌、介电性能和储能性能进行了研究。在25℃，1kHz条件下，该陶瓷的相对介电常数高达27480，介电损耗tan艿仅为4％，电滞回线形状细长，剩余极化很小，可释放的能量密度达0．31J·cm-3.结果表明：室温下该陶瓷具有优良的介电和储能性能。

简介：TheobjectiveoftheApollonprojectisthegenerationof10PWpeakpowerpulsesof15fsat1shot/minute.InthispapertheApollonfacilitydesign,thetechnologicalchallengesandthecurrentprogressoftheprojectwillbepresented.

简介：ThedemofacilityofchinaADSinjectorIIwasinstalledinthetunnelin2014.Theon-sitelayoutofdemofacilityisshownintheFig.1.ThedemofaclitymainlyincludesECRIS,LEBT,RFQacclerator,MEBTandTCM6.TheTCM6iscomposedbysixSCHWRcavity,sixSCsoleniodsandfiveBPMs.TheTCM6willbetheprototypeforthefuture2025MeVCADSsuperconductinglinac.ThebeamcommissioningofCADSInjectorIIstartedinJune2015.Itmainlyconsistsofthreesteps.

简介：TheZ=56bariumnucleirepresentoneofthebestexampleofanisotopicchaintoexploretheevolutionofquadrupoledeformationastheneutronnumberdecreases.Theneutron-deficientbariumisotopeswithmassnumberArangingfrom120to130couldbeeasilyproducedbytheheavy-ionfusionevaporationreactions,andthushavebeenwellstudiedinrayspectroscopyexperiments.

简介：氧化铝弥散强化铜合金是国际热核实验堆（ITER）的备选热沉材料之一,氘在其中的渗透滞留行为关系到ITER运行的安全性。通过气体驱动渗透平台测定了实验温度621~803K时氘气在氧化铝弥散强化铜合金中的渗透参数;通过热脱附谱实验平台记录了2种氧化铝弥散强化铜合金以及CuCrZr的热脱附曲线。结果表明：在相同温度区间内,氘气在氧化铝弥散强化铜合金中的渗透系数与纯铜及CuCrZr接近,说明氧化铝弥散相对氘气在氧化铝弥散强化铜合金中的渗透系数基本没有影响,而扩散系数比在纯铜和CuCrZr中都低,且在低温时显著降低;2种氧化铝弥散强化铜合金均有3个脱附峰,而CuCrZr合金只有1个脱附峰。

简介：

简介：用单辊甩带法制备了不含高生物毒性元素的Ti60Zr10Ta15Si15非晶薄带,并在高于其晶化开始温度的不同温度下对该非晶薄带进行了真空退火,研究了该非晶薄带在磷酸盐缓冲溶液（PBS）中的电化学腐蚀行为及热处理对其显微组织及其电化学行为的影响。结果表明,用单辊甩带法制备的Ti60Zr10Ta15Si15金属薄带为完全的非晶态结构,其玻璃转变温度和晶化开始温度分别为759K和833K,经过878K真空热处理后,薄带发生了部分晶化,在非晶的基底上析出了Ti相;经过938K热处理后,薄带发生了完全晶化,晶化相主要由Ti、Si3Ta5和SiZr以及TiSi组成。动电位极化测试表明,该非晶合金在PBS溶液中可表现出较为优异的耐蚀性能,部分晶化可进一步提高该合金的耐蚀性能,而完全晶化的合金抗腐蚀性能明显下降。