简介：Themechanicalproperties,creepdamage,creeprupturestrengthandfeaturesofinterfacialfailuresofweldedjointsbetweenmartensite(SA213T91)andpearlitesteel(12Cr1MoV)havebeeninvestigatedbymeansofargontungstenpulsedarcwelding,hightemperatureacceleratedsimulation,creeprupture,mechanicalpropertytestsandscanningelectronicmicroscope(SEM).Theresearchresultsindicatethatthemechanicalpropertiesofovermatchedandmediummatchedjointdeteriorateobviously,andtheyaresusceptibletocreepdamageandfailureafteracceleratedsimulationoperation500h,intheconditionofpreheat250℃,andpostweldingheattreatment750℃×1h.However,themechanicalpropertiesofundermatchedjointarethebest,theinterfacialfailuretendencyofundermatchedweldedjointislessthanthoseofmediumandovermatchedweldedjoint.Therefore,itisreasonablethatlowalloymaterialTR31isusedasthefillermetalofweldbetweenSA213T91and12Cr1MoVsteel.

简介：

简介：ButtjointsofQCrO.8/1Cr2lNiSTiequal-thicknessdissimilarmaterialswereobtainedbyelectronbeamweldingwithfixedacceleratingvoltage60kVandfocuscurrent1.99A,changedelectronbeamcurrentandweldingvelocity.MicrostructureandcompositionoftheEBWjointwereinvestigatedbymeansofopticalmicrographyandEDXanalysis,mechanicalpropertiesofthejointwerealsotested.Theresultsshowthatjoint'smacrostructurewasdividedintothreezones:topweldzonenearQCrO.8andbottomweldzoneconsistingofCu(ss.Fe)withacertainamountofdispersedlydistributed(α+ε)mixedmicrostructure,middleweldzoneconsistingof(α+ε)microstracturewithasmallamountofCu(ss.Fe)particles.MorphologicalinhomogeneousmacrostructureandunevenchemicalcompostionofQCrO.8/1Cr21NiSTijointbyEBWarethemostimportantfactortoresultindecreasingjoiningstrength.