简介：为了开发出新型的半导体光催化材料,本文基于液相激光熔蚀法,对钼酸银纳米粉末进行激光辐照,获得尺寸极小的钼酸银纳米晶.文章通过透射电子显微镜、XRD粉末衍射仪、拉曼光谱仪对该样品的形貌和结构进行了系列表征.紫外可见吸收光谱显示,钼酸银纳米晶在400~800nm波段具有吸收峰,通过Tauc公式拟合,得到该材料的光学带隙为2.4eV左右.以300W氙灯模拟自然光光源,对样品的可见光光催化降解甲基橙的降解效果进行了测定.

简介：WedevelopedadetailedsimulationmodeloftheArcticmarinetransportsystem(MTS)foroilplatformPrirazlomnaya.Themodelhasamultidisciplinarynatureandinvolves:sub-modelsofvarioustransportandtechnologicalprocesses;stochasticweathergeneratortoobtaintimeseriesof15environmentalparameters;andcontextualplanningalgorithmtobuildvoyageplanconsideringseveraltypesofshipsandcargoes.Weusedasignificantamountofrealoperationaldatatoidentifymodelparametersandtoproveitsstatisticalreliability.Ourmainscientifictaskistoinvestigatetheinteractionofvariousprocessesofadifferentnature,whilethepracticalaimistofindasetofmeasurestoincreasetheefficiencyofMTS.Theresultsofthestudyrevealmanyexamplesofthemutualinteractionofvariousprocessesthatneedtobeconsideredatthedesignstagetoavoidtechnicalmistakes.ThestudyformedabasisformakingmanagerialdecisionsatthetoplevelofGazpromNeftShelfCompany.

简介：本文运用主成分分析法能够对被评估对象评分、排序的功能，将主成分分析法应用于组合无形资产的分割评估中，确定组合无形资产中各单项无形资产的权重，进而正确界定其价值。

简介：提出了铁路车务站段调度人员综合评价方法，即利用主成分分析法对调度员综合素质进行评价。在计算的过程中，运用了SPSS软件，结果表明，运用主成分分析法对调度人员的综合素质进行评价是科学可行的。

简介：采用了SBS与橡胶改性剂复合改性制备高黏度改性沥青，研究了不同橡胶改性剂掺量制备改性沥青的性能，并研究了高黏度改性沥青排水沥青路面混合料的性能。结果表明：SBS与橡胶改性剂复合改性能够制备适合排水沥青路面的高黏度改性沥青，并得出了6％与8％是橡胶改性剂合适的添加掺量，研究出了适合排水沥青路面的高黏度改性沥青配方。

简介：采用氯化钠、多孔火山岩和石油树脂，按照优化配比和工艺制备了一种自融雪材料YjmpSalt。将TjmpSah按等体积法替代部分矿粉，添加到普通沥青混合料中，制作了不同YimpSalt掺量的沥青路面混合料对比试件。设计并实施了自然环境下各组试件的自融雪性能观测试验和氯化钠缓释性能观察试验，以及室内模拟结冰条件下的抑冰性能试验和结冰强度试验。结果显示，Timp—Salt掺量为7％的沥青混凝土路面具有良好的融雪、抑冰和缓释性能，其路用性能有所下降．但是可以满足规范要求。

简介：在Cu-Cr(其中Cr0.1～0.3wt%)二元合金基体上,利用B2O3、活性C和Ti在Cu-Cr合金溶液中的反应,原位生成TiB2颗粒增强铜基复合材料.探讨了其强化机理,测试了力学性能.结果表明:材料经处理后,其硬度为130HB,电导率为93.62%IACS,软化温度为510℃,抗拉强度为466MPa,屈服强度为420MPa,延伸率为22%,断口形貌的SEM照片呈现大量等轴韧窝,获得了一种综合性较好的Cu-Cr基复合材料.