简介：Thequenchsensitivityandtheirinfluentialfactorsof7,021,7,085,and7,050alloyswereinvestigatedbytheendquenchingtestmethodandthemeasurementofelectricalconductivity,hardness,andmicrostructureafteraging.Theresultsindicatethat7,050alloyhasthelargestchangeswithhardnessdecreasingfromHV199toHV167,andelectricalconductivityincreasesfrom16.6to18.2MSm-1whenthedistancefromquenchedendincreasesfrom2to100mm.Alloys7,085and7,021haverelativelysmallerchanges.Accordingtotherelationshipbetweenthehardnessandelectricalconductivityofasupersaturatedsolidsolution,7,050alloyhashigherquenchsensitivitythan7,085and7,021alloys.Themicrostructureof7,050alloywithhighermajoralloyelement(Zn+Mg+Cu)additionandCuelementadditionismostlyaffectedbythechangesofdistancefromquenchedend.In7,050alloy,thesizeofintragranularprecipitatesisfromabout10–200nm,andthe(sub)grainboundaryprecipitatesareabout20–300nm.Alloy7,085withlowerCucontentismoderatelyaffected,while7,021isleastaffected.Itisfoundthatwiththeincreaseofdistancefromquenchedend,quenched-inducedprecipitatepreferentiallynucleatesandgrowsinthe(sub)grainboundaryandthenonthepre-existingAl3Zrparticles.

简介：为改善La-Mg-Ni系A2B7型合金的电化学贮氢性能，在合金中添加一定量的Si元素，通过真空熔炼及退火处理的方法制备La0.8Mg0.2Ni3.3Co0.2Six（x=0-0.2）电极合金。研究Si元素的添加对合金结构及电化学贮氢性能的影响。结果表明，铸态及退火态合金均为多相结构，分别为Ce2Ni7型的（La,Mg）2Ni7相和CaCu5型的LaNi5相以及少量的残余相LaNi3。Si元素的添加没有改变合金的主相，但使得合金中的（La,Mg）2Ni7相减少而LaNi5相增加。添加Si显著地影响了合金的电化学性能。随着Si含量的增加，铸态及退火态合金的放电容量逐步降低，但循环稳定性却随着Si含量的增加而增强。此外，合金电极的高倍率放电性能、极限电流密度、氢扩散系数以及电化学交流阻抗谱的测试均表明合金的电化学动力学性能随着Si含量的增加先增加而后减小。

简介：采用分子动力学方法对Mg7Zn3合金快速凝固过程进行计算机模拟，研究玻璃转变过程局域结构与动力学之间的关联。结果表明：以Mg原子为中心的FK多面体和以Zn原子为中心的二十面体局域结构，对Mg7Zn3金属玻璃的形成起关键性作用。Mg（Zn）原子的扩散系数在熔点附近开始偏离Arrhenius关系，而满足幂指数规律。根据均方位移、非相干中间散射函数和非Gauss函数等时间相关函数，发现：随着温度的降低，β驰豫越来越显著，α弛豫时间以VFT指数规律迅速增加；而且半径较小的Zn原子比Mg原子呈现较快的弛豫动力学行为。另外，部分短程有序局域原子结构具有较慢的动力学行为，对β驰豫中笼子效应起主导作用；并随着其数目的大量出现，体系扩散系数开始偏离Arrhenius关系，玻璃形成过程微观结构转变温度TgStr与动力学转变温度Tc非常接近。