简介：TheDCcharacteristicsofSiGeHBTirradiatedatdifferentelectrondosehavebeenstudiedinacomparisonwiththoseofSiBJT.Generally,IbandIb-Ib0increase,Ic,Ic-Ic0andits+/-transitionVbeaswellasDCcurrentgainβdecreaseswithincreasingdose;increaseofIb-Ib0withincreasingdoseforSiBJTismuchlargerthanthatforSiGeHBT;βincreaseswithVbeorIb,butdecreasesatIb＜0.25mAwithIb,andcongregatesathigherdose;andadamagefactord(β)ismuchlessatthesamedoseforSiGeHBTthanforSiBJT.SiGeHBThasmuchbetteranti-radiationperformancethanSiBJT.SomeanomalousphenomenaforincreaseofIc,Ic-Ic0,Ib-Ib0andβatlowdosehavebeenfound.Someelectrontrapshavebeenmeasured.Themechanismofchangesofcharacteristicsisdiscussed.

简介：Thecharacteristicsoftemperatures,stressesandstrainsfieldshavebeenstudiednumericallyforatitaniumalloysheetweldedwithanimprovedgastungstenarcweldingmethod,inwhichatrailingspotheatsinkisintroducedtocontroltheweldingstressanddistortion.Theimpingingjetmodelisemployedtodescribetheintenseheattransferbetweenthecoolingmediaandthetopsurfaceoftheworkpiece.Theinfluenceofthedistancebetweenarcandheatsinkisinvestigated.Resultsshowthatthereisanidealrangeofdistance.Usingtheidealdistance,alowstressandnodistortionweldingstructurecanbederived.

简介：TheAl-alloyarc-weldingshapingsystembasedonarc-weldingrobotisestablished,andtheAl-alloyshapingmanufactureisrealizedwiththeDC(directcurrent)gasmetalarcwelding(GMAW).TheresearchindicatesthatthemetaltransfertypeofDCGMAW,heatinputandtheinitialtemperatureoftheworkpiecegreatlyaffecttheAl-alloyshapingbasedonarcweldingrobot.Onthepenetration,theweldwidthandthereinforcement,theinfluenceofweldingparametersisanalyzedbygeneralizedregressionneuralnetwork(GRNN)fitting.

简介：采用SEM、TEM、EDS、DSC、XRD和拉伸实验研究铸态7X50合金及其均匀化处理过程的组织演变。结果表明,铸态7X50合金相组成主要有S(Al2CuMg)、T(Al2Mg3Zn3)、MgZn2和少量的Al7Cu2Fe和Al3Zr相。均匀化处理过程中枝晶网和残留相逐渐减少,经(470°C,24h)+(482°C,12h)均匀化处理时,T相消失,S相有微量残留,Al7Cu2Fe相几乎没有变化。铸态合金的DSC曲线中在477.8°C处有一较强吸热峰,经470°C、1h均匀化后合金的DSC曲线在487.5°C处出现一个新的吸热峰,而经482°C、24h均匀化处理后合金在487.5°C处的吸热峰基本消失。在XRD谱中未出现T(Al2Mg3Zn3)相,这和T相与S(Al2CuMg)及MgZn2相相关的结论相吻合。预均匀化处理制备的板材中再结晶晶粒分数明显降低,抗拉强度和断裂韧性相对常规均匀化处理制备的板材分别提高约15MPa和3.3MPa·m1/2。

简介：为提高对时变信号的分析处理能力，设计了一组同时满足抗混淆、完全重构和正交化的Q—shift滤波器。与传统Q—shift滤波器相比，其权系数可以根据输入信号特性进行自适应调整。将基于自适应Q—shift滤波的双树复小波变换用于对超声缺陷信号进行阈值降噪，实验结果表明，与Q—shift10／10和DWT两种传统方法相比，去噪后信号的信噪比可以分别提高1．03dB和1．97dB。