简介:本《指南》编写依据:根据《船级社焊工考试委员会要求》和《船级社材料与焊接规范》编写而成。编写的目的是让焊工了解船舶焊接基础知识,掌握船舶焊接应知应会的施工常识和要求,了解焊工考试内容,提高焊工持证率。
简介:DD6alloywasbondedbytransientliquidphase(TLP)diffusionbonding.Themaincompositionsoftheinterlayeralloyemployedweresimilartothoseofthebasemetal,DD6,andacertainamountofelementBwasaddedasthemeltingpointdepressant.Theresultsshowthatitisdifficulttoobtainthejointswiththemicrostructurescompletelyhomogeneous.ForthejointTLPdiffusionbondedat1290℃for12h,abouthalfareasofthebeampossessedαγ+γ′microstructure,nearlyidenticalwiththatofthebasemetal,andtheotherlocalareasconsistedofT-solution,borides,etc.Prolongingthebondingtimeto24h,theinhomogeneousareasinthejointreduced,andthejointpropertyimproved.Thejointstress-rupturestrengthat980℃and1100℃reached90%-100%and70%-80%ofthoseofthebasemetalrespectively.
简介:BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope(SEM),electron.probemicroanalysis(EPMA)andX-raydiffraction(XRD).theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.
简介:WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability,evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.
简介:FlameheatingcombinedwithwatercoolingwasusedtostraightenA6N01aluminumalloyweldedjointandeffectofflameheatingpassonitsmicrostructureandmechanicalpropertieswasstudied.ResultsshowedthattheflameinducedtheprecipitationandgrowthoftheMg2SiphaseontheAlsubstrateforthethermalagingA6N01aluminumalloyweldedjoints,thusitledthedecreaseofmicro-hardnessandtensilestrengthoftheA6N01aluminumalloyweldedjointwiththeincreaseoftheheatingpass.However,thefatiguepropertyoftheflameheatedjointwasimprovedbecausetheMg2Siprecipitationhinderedtheinitiationandpropagationofthefatiguecrack.
简介:本文介绍了低温(-50℃)乙烯球罐制造和焊接技术,制定了球罐制造工艺流程和球壳板成形工艺,通过试验确定了焊接预热温度、层间温度和后热温度,并正确选择了焊接材料。制定了乙烯球罐的焊接工艺规范,并成功地完成了低温(-50℃)乙烯球罐的制造和焊接。
简介:ThispaperintroducesabrazingprocessbetweenAl_2O_3ceramicandInvaralloy.Al_2O_3canbebrazedwithInvareffectively.TheinterfacialstructureofAl_2O_3/Invarjointcanbeexpressedas:Invar/Ag(s,s)+Cu(s,s)+Fe_2Ti(zoneⅠ)/Ag(s,s)+Cu(s,s)+Fe_2Ti+NiTi+Cu_3Ti(zoneⅡ)/Ag(s,s)+Cu(s,s)+Cu_2Ti+Al(s,s)+TiC+TiO(zoneⅢ)/Al_2O_3.Themaximumshearstrengthof139MPawasmeasuredforas-brazedAl_2O_3/Invarjointbrazedat850℃for25minor900℃for15min.
简介:Inthispaper,6mmthick2219-T6aluminumalloywasjoinedbymeansofvariablepolaritytungsten-arcwelding(VP-TIG)andtheinfluenceofgradientmismatchesonVP-TIGjointsisinvestigated.Theaveragetensilestrengthofthejointsreduces32%,53%and59%,whenthemismatchofthejointwas0.635mm,1.44mm,1.83mm,respectively.Incompletepenetration,additionalbendingmoment(Ma)anddecreaseofeffectiveloadregionareaareconsideredtoexplainthisphenomenon.Thefracturelocationoftensilespecimensoccurredattheweldzone(WZ)closetopartialmeltzone(PMZ),correspondingtoasharpdeclineofmicrohardnessfromPMZtoWZ.Theoriginalpositionoffractureisfoundatweldtoe,whereincompletepenetrationformsduetotheintroductionofgradientmismatches.
简介:Dynamicsinpartialtransientliquidphasebonding(PTLPbonding)ofSi3N4ceramicwithTi/Cu/Timulti-interlayerwassystematicallystudiedthroughmicro-analysisofjointinterfaces.Theresultsshowthatgrowthofreactionlayerandisothermalsolidificationprocessiondoatthesametime.GrowthofreactionlayerandmovingofisothermalsolidificationinterfaceobeytheparaboliclawgovernedbythediffusionofparticipatingelementsduringthePTLPbonding.Coordinationoftheabovetwodynamicsprocessisdonethroughtimeandtemperature.Whenreactionlayerthicknessissuitableandisothermalsolidificationprocessisfinished,thehighbondingstrengthatroomtemperatureandhightemperatureareobtained.
简介:Anewhardfacingprocess,reactivebrazecoatingprocess(RBCC)wasstudied,and(TiC+Cr3C2)/FecompositecoatingswerepreparedbyRBCCusingcarbon,Cr3C2,iron,ferrochromiumandtitaniumpowderastherawmaterialsinvacuumbrazefurnace.TheresultsshowthatTiCisin-situsynthesizedinthecoatings.ThemethodsofintroducingCr3C2havegreateffectsonthedistributionofTiC.AddingCr3C2directlytotherawmaterialsforcoatings,fineTiCparticlesaggregateintodiscoidsparalleltothecoatingsurface,whereas,in-situsynthesizingCr3C2incoatings,theaggregationsofTiCarelumpish.Duringbrazecoating,Cr3C2particlesdirectlyaddeddissolveandprecipitatetobecomeneedle-shaped.Thecoatingshaveanevenandsmoothsurfaceandarecombinedwiththeirmildsteelsubstratesbyametallurgicalbonding.
简介:Stationaryshoulderfrictionstirlapwelding(SSFSLW)wassuccessfullyusedtoweld6005A-T6aluminumalloyinthispaper.EffectofpinrotatingspeedoncrosssectionmorphologiesandlapshearstrengthoftheSSFSLWjointsweremainlydiscussed.Resultsshowthatjointswithoutflashandshouldermarkscanbeobtainedbythestationaryshoulder.CrosssectionoftheSSFSLWjointpresentsabasin-likemorphologyandlittlematerialloss.Byincreasingtherotatingspeedfrom1000rpmto1600rpm,botheffectivesheetthicknessandlapwidthincrease,whilelapshearfailureloadfirstlydecreasesandthenincreases.Themaximumfailureloadof14.05kNisattainedwhen1000rpmisused.AllSSFSLWjointspresentshearfracturemode.
简介:TheHAZmicrostructureandperformanceofQuenchingandTemperingmodetemperbeadweldingandgeneralweldedjointswhichweremadeonSA508-3steelof60mmthicknesswerecomparedinthisarticle.Theresultshowsthattemperingsorbitewhichhasexcellentoverallperformancewasobtainedinbothmodes.ThemicrostructureofQuenchingandTemperingmodeweldedjointsgotmorefinegrain.Eventhoughthehardnessoftemperingbeadweldedjointsishigherthanthegeneralone,itstillmeetsthestandardswhichislowerthan350HV.TheimpactabsorbingenergyofeachdistrictoftemperingbeadweldedjointsHAZreached170J,whichisequaltogeneralone.