简介:Al2O3-MgOcastableshavebeenwidelyusedforworkingliningsofsteelladleduetotheirsuperiorhotstrengthandcorrosionresistance.Inthiswork,effectsofmicrosilica,ultrafinealuminaandMgOfinesadditionsontherheologicalbehaviorofthecastableswereinvestigatedbymeansofIBBrheometerV1.0tomeasuretorque(shearstress)undervaryingshearrates.Theresultsshowthatrheologicalpropertiesofcastablesatvaryingshearratesaresignificantlyimprovedwithincreaseofmicrosilicaadditions(from1mass%to5mass%)andcorrespondingdecreaseinwateraddition;thereisonlylittlechangeinrheologicalbehaviorwithvariationofultrafinealuminaandMgOfinesadditions.Optimumultrafinealuminaandmicrosilicaadditionsarerecommendedforcastableswithgoodrheologicalbehavior.
简介:Researchonnewtypesofcastables,pre-castassemblypartsandthermalinsulationmaterialswithgoodresistancetowear,thermalshockanderosion,andlowthermalconductivity,wasdonetosolveproblemsofhighsystemenergyconsumption,crackingandspallingofpartialliningandmismatchoffurnacetopmaterialandhangingmaterialandsoon,causedbyunreasonabledesignofChina'sAl(OH)3dilutephasefluidizedbedroastingfurnacelining.Severaldifficultproblemssuchasthematchingofdifferentmaterials,preservationofexpansionjointsamongdifferentzonesandreasonablemechanicaldistributionofliningweresolved.'Integratedfurnace'conceptwasestablishedincludingrefractoriesR&D,liningstructuredesign,constructionoptimization,furnacewarmingtechnology,initialoperationandliningmaintenancetechnology.Thekeytechnologiesofhigh-efficiencyandenergy-savingforfurnacesweredeveloped.TheseachievementshavebeenappliedtoChina'sAl(OH)3dilutephasefluidizedbedroastingfurnacestoreduceenergyconsumptionby1000MJpertonalumina,enhancethecapacityandreducetheexhaustgasemission.